NON METALLIC
SANITARY CLAMP |
|
Sanitary Ferrule Clamp
• Constructed of Non-Metallic fiberglass
reinforced nylon.
• Accepts sanitary ferrules according to
BS 4825, ISO 2852 and Tri-Clover® Standards.
• Will not cause distortion in non-metallic
ferrules, as will stainless steel clamps
during high operating temperatures and sterilization. Less weight than stainless
steel clamps.
• Use where reduction of weight and
reduced thermal conductivity transfer is
of importance.
• Use on non-metallic to non-
metallic, nonmetallic
to metallic and metallic to metallic sanitary mechanical joints. |
Tests and Operating Capability
• For use in GMP Manufacturing
• Gamma stable to 25-40 kGy
• Maximum irradiaton dosage is 6 mega rads, this dosage is cumulative. Expect to see discoloration and the material to become brittle.
•Autoclave Sterilize to 275°F (135°C) After autoclave clamp may need to be retorqued
•Maximum recommended installation
torque specification is 2nm.
• Recommended working pressure, 150 p.s.i. @ 70°F
• PTFE gaskets are not to be used in conjuction with the non metallic clamp. Acceptable elastomers are: Tuf-Flex®, Silicone, FKM, EPDM.
|
|
|
|
SIZE |
A DIM. |
B DIM. |
R DIM. |
Max p.s.i. |
1/2" & 3/4" |
2.17" |
.749" |
.394" |
150 |
1" & 1-1/2" |
3.94" |
.749" |
.886" |
150 |
2" |
4.64" |
.749" |
1.26" |
150 |
2-1/2" |
5.20" |
.749" |
1.497" |
150 |
3" |
5.75" |
.749" |
1.773" |
150 |
4" |
6.66" |
.749" |
2.25" |
150 |
Tensile Strength (MPa) |
Tensile Strength |
Flexural Modulus (MPa) |
Heat Deflection |
Water Absorption |
Nylon Resin used in the Clamp |
195 Mpa
ISO 527 |
10000 Mpa ISO 527 |
261° C
@ .45 Mpa
ISO 75f |
1.9% @ 50% RH
similar to
ISO 62 |
*Maximum Recommended Working Temperature is 200° F |
| |
|
|